CEM-3
CEM-3 |
| |||||
| |||||
(ULANSI:CEM-3) | |||||
| |||||
特色
| 運用範疇 | ||||
| |||||
FEATURES
| APPLICATIONS | ||||
| |||||
GENERAL PROPERTIES | |||||
Test Item | Test condition | Units | Standard value | Typical value | |
1.Peel Strength , IBS/IN,Minimum,1 OZ |
| IBS/IN |
|
| |
As received | A | ≥8.0 | 12.5 | ||
After thermal stress | A | ≥8.0 | 12.5 | ||
2. Volume resistivity ,Minimum | E-24/125 | MΩ.cm | ≥103 | ≥106 | |
3. Surface resistivity , Minimum | E-24/125 | MΩ | ≥103 | ≥106 | |
4.Water absorption , Maximum | E-1/105+des | % | ≤0.50 | 0.23 | |
5.Dielectric Breakdown, Minimum | D-48/50 D-0.5/23 | Kv | ≥40 | 42 | |
6. Flexural strength ,Minimum |
| Mpa |
|
| |
Length direction | A | ≥276 | 390 | ||
Cross direction | A | ≥186 | 320 | ||
7.Arc resistance ,Minimum | D-48/50 | S | ≥60 | 115 | |
8.Flammability | A | S | UL-94V0 | UL-94V0 | |
9. Permittivity 1MHZ ,Maximum | A |
| ≤5.4 | 4.6 | |
10.Loss tangent 1MHZ ,Maximum | A | --- | ≤0.035 | 0.02 | |
11.Thermal stress 260℃,10sec( Minimum ) |
| --- |
|
| |
Non etched specimen | A | NO DEFECT | NO DEFECT | ||
Etched | A | NO DEFECT | NO DEFECT | ||
12. TG(DSC,℃) | A | ℃ | ≥135 | 136 | |
13. CTI,V | TEC-112 | V | ≥175 | 200 | |
Note: |
Warpage of Warpage of
(No-treating) (After treating:125℃ 2hr)
Peel strength
※Specimen T hickness:1.6mm single side board
PURCHASING INFORMATION |
| ||
Thickness | Copper foil | Standard Size |
0.8mm to 3.4mm | 12μm to 105μm | 1041×1245mm(41″×49″) 940×1245mm(37″×49″) |
※ Other sheet size and thickness could be available upon request. |
相幹2022年澳门天天彩开奖结果图産品
産品征詢
若是心水是什么意思网络语您對我們的産品有任何樂趣心水是什么意思网络语,歡迎隨時給我們畱下您的意曏信息
台灣刘百温930十码期期准諾德新材料股分刘百温930十码期期准有限公司
地址:如東縣經濟開辟澳门平特怎样公式计算方法區鴨綠江路98號
傳真:0513-84885522
網址:www.ccl-roda.com
郵箱:sales@ccl-roda.com
Copyright © 2021 台灣諾德新材料股分有限公司 版權壹切. 甦ICP備11031610號 技術支撐:中企動力中壢